Nickel-based alloys are known for their excellent corrosion resistance and high-temperature strength. However, at high temperatures, polycrystals experience grain boundary-stress-driven vacancy diffusion leading to diffusion-driven creep. Understanding the fundamentals of defect migration is essential to predict diffusion creep behavior. In this talk, we explore the Nabarro-Herring diffusion creep and the associated solute segregation that is likely to result from the different diffusivities of the solute and solvent elements. Density functional theory calculations are performed to determine the formation, migration and binding energies of the solute and vacancy defects in stress-free and stressed states. The dilute-limit transport coefficients are then calculated using the self-consistent mean field theory as implemented in the Kinetic Cluster Expansion (KineCluE) code. Predictions of diffusion creep strain rates and solute segregation are then presented for various solutes, stress and temperatures. This work opens research avenues for exploration of diffusion creep via characterization of elemental segregation to grain boundaries.