The main objective of this project was to conduct a comparative assessment between the optical dilatometer method and resistivity method, using all 10 SiC temperature monitors provided by two Nuclear Science User Facility experiments: BSU-8242 and General Electric Hitachi. Unfortunately, due to multiple delays in acquiring, shipping, and cleaning the SiC temperature monitors, the project was only able to process one (1) SiC temperature monitor during this period. SiC temperature monitor KGT-3357 was evaluated via the optical dilatometer method to determine its peak irradiation temperature. The KGT-3357 sample was from the BSU-8242 experiment and designed for a temperature of 300°C and an exposure of 1 dpa. The optical dilatometer measurements indicated that the KGT-3357 SiC temperature monitor’s peak irradiation temperature range was 240–267°C, with sensitivity of approximately ±20°C. Additionally, this temperature range falls within the evaluated melt wire temperature range of 238.6–271.5?. The remaining six (6) SiC temperature monitors from the BSU-8242 experiment and three (3) from the General Electric Hitachi experiment will be used in the future work to further validate the optical dilatometer method for measuring SiC peak irradiation temperatures.