This report summarizes the work performed at Idaho National Laboratory under the “Creep, fatigue and creep-fatigue crack growth tests” task of the “Long-Term VHTR Material Qualification – INL” work package. Work was performed this year to validate the crack growth monitoring setup used with the test frames against both continuous crack length monitoring using an optical camera, as well as post-mortem analysis of marker bands on the fracture surface. Delays prevented the use of a gauge to measure load-line displacement for early tests, and so the creep-fatigue crack growth setup was evaluated using the actuator displacement for a load-line displacement setup. While not ideal, this allowed examination of the shortcomings with the current software setup that was originally designed for performing stress corrosion crack growth rate studies. The method for data collection was modified to link the crack growth monitoring software with Instron’s Wave Matrix software. Once the load-line displacement gauge arrived, the crack growth equipment was successfully modified to permit continuous monitoring of both load-line displacement and crack length. This is critical for creep-fatigue and creep crack growth rate studies for ductile material, as it permits the C* and Ct analyses. Test results are shown for Alloy 617 fatigue and creep-fatigue (without the gauge for load-line displacement measurements), as well as creep-fatigue of Alloy 709, which was performed with the completed test setup, allowing for crack length and load-line displacement monitoring.