Idaho National Laboratory (INL) initiated a joint international effort with the Czech Republic to explore the feasibility of manufacturing High Entropy Alloys for high-temperature nuclear applications using Additive Manufacturing. This effort was funded at INL by the United States Department of Energy’s Office of Nuclear Energy under the Advanced Reactor Technologies and Advanced Materials and Manufacturing Technologies (AMMT) Program. The High Entropy Alloys were specifically designed for the corrosive and irradiation environments as experienced in gas fast reactors, molten salt reactors, and fusion power. These alloys were manufactured by multiple processes to determine the impact of manufacturing processes on the performance of the alloys in corrosive and irradiation environments. Preliminary results show that MoNbTiV and MoNbTi alloys exhibit no degradation after multiple corrosion tests. These MoNbTiV and MoNbTi alloys were also evaluated after irradiation experiments were conducted at the Michigan Ion Beam Laboratory at the University of Michigan, which is the focus of this milestone report. For these irradiation experiments, the MoNbTiV and MoNbTi alloys manufactured by arc melting and Electric Field Assisted Sintering (EFAS) were tested at 500 C at a dose of 30 dpa to evaluate the microstructural stability and decomposition.