Four post-irradiation heating tests of fuel compacts from the U.S. Advanced Gas Reactor (AGR)-3/4 irradiation experiment were completed. In addition to tristructural isotropic (TRISO)-coated driver fuel, each compact contained designed-to-fail (DTF) particles with fuel kernels coated only in pyrocarbon so as to simulate exposed kernels. Tests at 1600/1700°C, 1400°C, and 1200°C were performed to measure fission product release as a function of time and temperature. Silver release was highest in the 1200°C test, supporting the observation that silver release rates are highest in the 1100–1300°C range. Compared to tests of AGR-1 compacts with no exposed kernels, the Cs-134 and Kr-85 releases were noticeably higher in AGR-3/4. The exposed kernels’ contributions to Eu and Sr release are inconclusive, due to the difficulty in distinguishing among the combined effects of higher irradiation temperatures in these particular AGR-3/4 compacts, the presence of the DTF particles, and the Fuel Accident Condition Simulator (FACS) test temperatures. These data can be used to make inferences about fission product retention in exposed kernels as a function of time and temperature.