To support the technical basis for the extended dry storage of aluminum-clad spent nuclear fuel (ASNF), thermal pretreatment procedures to minimize the radiation-induced generation of molecular hydrogen (H2) have been investigated. The aim of thermal pretreatment is to eliminate the residual adsorbed water content on the ASNF’s corrosion layers, precursors for H2 generation. To date, irradiation studies in this area have found conflicting results for the effectiveness of thermal pretreatment procedures. The aim of this study was to reconcile those differences. However, the presented results, which utilized a modified in situ thermal pretreatment procedure, afforded H2 yield data that further indicates that thermal pretreatment does not significantly reduce the radiation-induced yield of H2 from gamma irradiated ASNF surrogate materials. Assessment of the differences between thermal pretreatment studies suggests that stainless-steel—present in the irradiation setup of studies that demonstrated a reduction in the yield of H2 with thermal pretreatment—may afford not only unanticipated interfacial chemistry, but also the formation and radiolytic contribution of iron oxides to the chemistry underpinning the formation of H2 in these systems. Given the Department of Energy Standard Canister—proposed for the extended dry storage of ASNF—is predominantly composed of stainless-steel, the potential contribution of stainless-steel and its corrosion layers to radiolytic H2 production should be further investigated. This research was funded by the U.S. Department of Environmental Management, Office of Technology Development, under contract DE-AC07-05ID14517.