A plate-type nuclear fuel consisting of a solid monolithic foil of U-10wt%Mo is under development for use in the United States’ high performance research reactors. In support of developing this fuel, the fuel has been fabricated for the first time by a commercial fuel vendor and subsequently irradiated in a test reactor. This provides an opportunity to evaluate post-irradiation mechanical properties of the commercially fabricated fuel. Four-point bend testing was conducted on the irradiated U-10Mo fuel and the data produced includes bending strength and Young’s modulus. Although the material behaves in a brittle manner due to the developed porosity, a general trend of strength and modulus reduction are found as fission density increases. The data produced is evaluated using both Weibull statistics and a modulus degradation model with recommendations provided.