Molten salt reactors (MSRs) are gaining attention due to their potential for safe, carbon-free nuclear energy with reduced waste. However, licensing these reactors is hindered by limited experimental data on fueled salts, both pre- and post-irradiation. The novel Molten-salt Research Temperature-controlled Irradiation (MRTI) vehicle was designed to address knowledge gaps in irradiating enriched-uranium-bearing salts. The MRTI experiment irradiated 13 cm3 of UCl3-NaCl (93% U-235) salt in the Neutron Radiography (NRAD) Reactor, achieving a burnup of 0.196 GWd/MTU over 390 hours. Despite a heater failure, the thermocouple data suggested fission heat kept the salt molten. The MRTI assembly was remotely disassembled for nondestructive post-irradiation examination (PIE), which included precision gamma-ray scanning (PGS) and neutron radiography. Radiograph images showed the location of th mol%e salt and the solidification pattern. PGS results provided an early indication that activated materials of construction did not increase in relative intensity in the region of the capsule where the salt was in contact with the material of construction. Additionally, PGS data showed the presence of several gamma emitting fission products, such as Nb-95, Zr-95, Ru-103, Ce-141, and La-140, where Ru-103 had the highest counts at the bottom of the capsule. Computational fluid dynamics modeling supported observations of salt solidification patterns and proved to be a valuable tool to inform PIE activities. The MRTI experiment has thus far provided critical data and lessons learned for fuel salt PIE activities, essential for advancing the technical readiness of MSRs.