The Advanced Fuels Campaign Fission Accelerated Steady-state Test (FAST) at Idaho National Laboratory (INL) completed its first irradiation cycle within the Advanced Test Reactor (ATR). The test focused on the irradiation of alloy fuel forms for use in sodium fast reactors. Tests included the use of fuel additives (Sn, Sb, and Pd) for reducing the gettering of lanthanide fission products, zirconium liners to mitigate fuel-cladding chemical interaction, and annular fuel geometry for sodium-free fuel designs. The first cycle of FAST testing was completed and a series of rodlets were removed for the initial post irradiation examination (PIE) of FAST rodlets. The rodlet irradiation conditions was evaluated using Monte Carlo N-Particle (MCNP) for as-run power history and COMSOL for temperature analysis. These rodlets include a set of low burnups (~2.5 % heavy metal [%FIMA]) control rodlets and a helium bonded annular rodlet (4.7 %FIMA). Initial non-destructive PIE has been completed and includes, visual inspection, neutron radiography and gamma scanning of the FAST rodlets. Radiography confirmed the integrity of the experiments as well as showing the complete filling of the annulus in the annular fuel at a modest burnup (4.7 %FIMA) and potential slumping of the cooler rodlets at lower burnup. Precision gamma scanning indicated mostly usual fission product behavior with the exception of the ceasium in the He-bonded annular fuel. Future destructive PIE will be necessary in order to fully understand the effects of accelerated irradiation on U-Zr metallic fuel behavior.