Corrosion of 316L Stainless Steel Under the Natural Circulation of Molten NaCl-MgCl2 Salt
The corrosion behavior of 316 stainless steel (SS) was studied in the natural circulation of eutectic molten NaCl-MgCl2 salt using the microloop concept. The post-corrosion tested 316 SS microloop sections were characterized with microscopy techniques to understand the microstructural and microchemical changes that occurred at the alloy/salt interface. It was found that 316 SS showed […]