Corrosion mitigation has long been considered a challenge in long-term service of both pyrochemical reprocessing and molten salt reactor applications. Corrosion coupons consisting of 2.25Cr 1Mo ASME SA387 Grade 22 Class 2 steel, were installed in a uranium electrorefiner containing molten chloride salt at 500°C. This electrorefiner went into service at Idaho National Laboratory in 1994. Seven of these coupons were removed in 2019 (i.e., submerged in molten salt for 25 years) for analysis and characterization including neutron imaging, optical microscopy, scanning electron microscopy, and wave/energy dispersive x-ray spectroscopy. The results showed that all seven coupons experienced between 30 to 175 µm of surface degradation without evidence of brittle fracture. Meaning there was no evidence of accelerated corrosion or fractures, and the average steel surface loss was of less than 5 µm per year. All indications were that the environmental conditions inside the electrorefiner were favorable for the steel alloy.