The development of a new ASTM standard for evaluating the corrosion resistance of additive manufactured (AM) stainless steel (SS) 316H in chloride molten salts is critical for the use of these materials in extreme environments such as molten salt reactors (MSRs). This report pertains to a work package of the Advaned Materials and Manufacturing Technologies (AMMT) developing a systematic methodology to link changes in AM fabrication parameters, namely surface finishing, porosity, microstructure, and chemical heterogeneity, to corrosion performance in NaCl-MgCl2 salt, a proposed secondary coolant for MSRs. During Fiscal Year 2024, Idaho National Laboratory investigators in the AMMT program, utilized SS316H bars, fabricated with laser bed powder fusion at Los Alamos National Laboratory, to establish and optimize the workflow for evaluating these process-to-performance relationships. Standard practices for specimen preparation were established using these specimens, with particular focus on descaling and sectioning methods that align with ASTM guidelines. A comprehensive experimental design for static corrosion testing was developed, with pre- and post-exposure analysis utilizing optical microscopy and scanning electron microscopy. So far standard descaling techniques were optimized, one static corrosion test was conducted on the LANL AM SS316H specimens, and pre- and post-corrosion practices were established. In addition, the work package yielded a review paper on corrosion testing gaps for AM materials in nuclear applications and submitted a proposal for a rapid-turnaround experiment to the Nuclear Science User Facilities Program to investigate the combined effects of proton irradiation and corrosion on AM SS316H. This work package establishes a foundation for evaluating processing-to-performance relationships for AM SS316H in harsh conditions, contributing to the safe and efficient design of components for next-generation nuclear reactors. The creation of a standardized methodology and the generation of relevant publications and future research pathways represent significant strides towards integrating AM materials into critical applications where corrosion resistance is paramount.